BULLSEYE COLORS & SCHEDULES
YOU CAN GET AN ONLINE EDUCATION AT BULLSEYE GLASS
CLICK THE AD BELOW TO SEE
BULLSEYE GLASS COLORS
(COLOR MAY VARY DEPENDING ON YOUR MONITOR)
WHITE 0113 |
BLACK 0100 |
LT PEACH CREAM 0034 |
ERBIUM PINK 1821 |
TURQUOISE OPAL 0116 |
SALMON PINK 0305 |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
|
|||||
PINK 0301 |
CRANBERRY PINK 1311 |
GOLD- PURPLE 0334 |
LIGHT PLUM 1405 |
LIGHT VIOLET 1428 |
VIOLET STRIKER 1234 |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
|
|||||
DEEP ROYAL PURPLE 1128 |
LIGHT AMBER 1437 |
CHARTREUSE 1426 |
LIGHT BRONZE 1409 |
MEDIUM AMBER 1137 |
SUNSET CORAL 1305 |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
|
|||||
WOODLAND BROWN 0203 |
POWDER BLUE 0108 |
LT AQUAMARINE BLUE 1408 |
TURQUOISE BLUE 1116 |
NEO- LAVENDER 0142 |
LT SKY BLUE 1414 |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
|
|||||
COBALT BLUE 0114 |
DEEP ROYAL BLUE 1114 |
DARK COBALT 0147 |
MIDNIGHT BLUE 1118 |
AQUAMARINE BLUE 1108 |
LT STEEL BLUE 0146 |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
|
|||||
EGYPTIAN BLUE 0164 |
STEEL BLUE 1406 |
CANARY YELLOW 0120 |
SUNFLOWER YELLOW 0220 |
MARIGOLD YELLOW 0320 |
PUMPKIN ORANGE 0321 |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
|
|||||
ORANGE 0125 |
RED 0124 |
FRENCH VANILLA 0137 |
DRIFTWOOD GRAY 0132 |
DECO GRAY 0136 |
LT SILVER GRAY 1429 |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
|
|||||
CHARCOAL GRAY 1129 |
MINT GREEN 0112 |
SPRING GREEN 0126 |
LIGHT GREEN 1107 |
EMERALD GREEN 1417 |
TEAL GREEN 0144 |
![]() |
![]() |
![]() |
![]() |
![]() |
![]() |
|
|||||
LIGHT ADVENTURINE 1412 |
JADE GREEN 0145 |
ADVENTURINE GREEN 1112 |
KELLY GREEN 1145 |
OLIVE GREEN 1141 |
|
![]() |
![]() |
![]() |
![]() |
![]() |
|
BULLSEYE FULL FUSE FIRING SCHEDULES
THESE ARE SUGGESTED STARTING POINTS. ALL KILNS ARE DIFFERENT. EXPERIMENT! THIS SCHEDULE ASSUMES A 3mm THICKNESS OF GLASS (1 LAYER) WITH PERHAPS SOME FRIT ON TOP |
||||
SEG. |
RAMP deg. F./hr |
TEMP deg. F. |
HOLD minutes |
EXPLANATION |
1 | 400 | 850 | 10 | Slow heat to avoid thermal shocking of the glass. |
2 | 600 | 1100 | 00 | Standard ramp rate |
2 | 100 | 1250 | 30 | Very slow ramp rate to "squeeze" the bubbles from the glass and anneal soak. |
4 | AFAP | 1500 | 5 | As Fast As Possible to full fuse temperature |
5 | AFAP | 960 | 60 | As Fast As Possible to Bullseye annealing temperature with annealing hold. |
6 | 300 | 100 | 00 | Slow cool to reduce thermal shocking. |
NOTE: If you add frit on top, this will give a smooth color finish. If you want a more textured look, change segment 4 temp. to 1380 deg. F. | ||||
THIS SCHEDULE ASSUMES 6-9mm THICKNESS OF GLASS (2 -3 LAYERS) | ||||
SEG. |
RAMP deg. F./hr |
TEMP. deg. F. |
HOLD minutes |
EXPLANATION |
1 | 300 | 850 | 15 | Slow heat to avoid thermal shocking of the glass. |
2 | 500 | 1100 | 00 | Slightly less than standard rate. |
3 | 100 | 1250 | 30 | Very slow ramp rate to "squeeze" the bubbles from the glass and anneal soak. |
4 | AFAP | 1500 | 10 | As Fast As Possible to full fuse temperature. Five minutes longer hold. |
5 | AFAP | 960 | 120 | As Fast As Possible to Bullseye annealing temperature with annealing hold. |
6 | 100 | 700 | 00 | Very slow rate because of thickness of glass until below annealing range. |
7 | 300 | 100 | 00 | Slow cool to reduce thermal shocking. |
BULLSEYE SLUMPING SCHEDULES
THIS SCHEDULE ASSUMES 6-9mm THICKNESS OF GLASS (2 -3 LAYERS) | ||||
SEG. |
RAMP deg. F./hr |
TEMP. deg. F. |
HOLD minutes |
EXPLANATION |
1 | 200 | 900 | 15 | Slow heat to avoid thermal shocking of the glass. |
2 | 100 | 1175 | 2.5 hrs | Allow full slumping. If watching, can stop when satisfied. |
3 | AFAP | 960 | 40 | Anneal time to allow glass to stabilize. |
4 | 100 | 800 | 00 | Very slow rate as glass returns to solid state. |
5 | 200 | 700 | 30 | Slow cool to reduce thermal shocking. |
6 | 400 | 100 | 00 | Final cooling. Don't open kiln above 100 degrees. |